PENGARUH VARIASI KOMPOSISI DAN TEMPERATUR ANNEALING PADA PEMBUATAN LAPISAN TIPIS BARIUM ZIRKONIUM TITANATE DENGAN MENGGUNAKAN METODE SOL-GEL

Simple item page
dc.contributor.authorFitriani, Nisya Adia
dc.contributor.supervisorDewi, Rahmi
dc.date.accessioned2022-01-19T03:27:59Z
dc.date.available2022-01-19T03:27:59Z
dc.date.issued2021-07
dc.description.abstractBarium Zirconium Titanate (BZT)) thin layer is the most interesting material to be studied because it has a high dielectric constant. A thin film of Barium Zirconium Titanate fabricated with sol-gel method with composition of x= 0.80 and x= 0.85 was annealed with temperature variation of 550°C, 600°C and 650° C 1 hour. Barium Zirconium Titanate thin films characterized using X-Ray Diffraction (XRD). Based on the XRD pattern, the lattice parameters, crystal structure, and crystal size can be determined. Crystal size was calculated based on diffraction pattern using the Scherrer formula. The result shows that annealing temperature affects the crystal size of the samples. The value of lattice parameters of a = b for composition x = 0.80 is 3.74 Å and for the value of c is 3.91 Å , while for composition x = 0.85 shows the value of a = b is 3.72 Å and for the value of c of 4.25 Å. The crystal size for x = 0.8;0.85 with a temperature of 550oC, 600oC and 650oC are 22,56 nm, 29,02 nm, 32,49 nm, 35,33 nm, 42,76 nm and 50,78 nm. respectively. This result shows the crystal structure of BZT is tetragonal since the value of the lattice parameter were a=b c.en_US
dc.description.sponsorshipProgram S1 Fisika FMIPA-Universitas Riau Fakultas Matematika dan Ilmu Pengetahuan Alam, Universitas Riauen_US
dc.identifier.otherwahyu sari yeni
dc.identifier.urihttps://repository.unri.ac.id/handle/123456789/10421
dc.language.isoenen_US
dc.publisherperpustakaan URen_US
dc.subjectBarium Zirconium Titanateen_US
dc.subjectSol Gel Methoden_US
dc.subjectAnnealingen_US
dc.subjectXRD Characterizationen_US
dc.titlePENGARUH VARIASI KOMPOSISI DAN TEMPERATUR ANNEALING PADA PEMBUATAN LAPISAN TIPIS BARIUM ZIRKONIUM TITANATE DENGAN MENGGUNAKAN METODE SOL-GELen_US
dc.typeArticleen_US

Files

Original bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
NISYA_ADIA_FITRIANI_compressed.pdf
Size:
219.92 KB
Format:
Unknown data format
Description:
artikel
Download
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
license.txt
Size:
1.71 KB
Format:
Item-specific license agreed upon to submission
Description:
Download

Collections

Physics