Binderless composite electrodes in the monolithic form prepared from carbon nanotubes (CNTs) and self‐adhesive carbon grains (SACG) from fibers of oil palm empty fruit bunch were studied as an electrode in a supercapacitor. ...

Self-adhesive carbon grains (SACG) was prepared from fibers of oil palm empty fruit bunches. The SACG green monoliths were carbonized in N2 environment at 400, 500, 600 and 700°C to produce carbon monoliths labeled as CM1, ...

Fibers of oil palm empty fruit bunches were used to produce self-adhesive carbon grains (SACG). The SACG green monoliths were carbonized in N2 environment at 800°C to produce carbon monoliths (CM) and the CM was CO2 activated ...

Activated carbon powders (ACP) were produced from the KOH treated pre-carbonized rubber wood sawdust. Different conductive materials (graphite, carbon black and carbon nanotubes (CNTs)) were added with a binder (polivinylidene ...

The green monoliths (GMs) were prepared from the mixtures of pre-carbonized fibers of oil palm empty fruit bunches (or self-adhesive carbon grains (SACG)) and green petroleum coke (GPC) with the mixing ratio of 0, 10, 30, ...

Binderless activated carbon monoliths (ACMs) with high porosity that were prepared from self-adhesive pre-carbonized rubber wood sawdust were studied as electrodes for supercapacitors, focusing on the influence of activation ...

Amongst the current trend in the study of carbon composite electrodes is the addition of carbon nano particles, without binding materials, into conventional carbon to produce electrode in order to benefit from both the ...

Binderless composite monolith (BCM) electrodes prepared from carbon nanotubes (CNTs) and self-adhesive carbon grains (SACGs) were used in a symmetrical supercapacitor. The SACGs were prepared from fibers of oil palm empty ...