  • No Thumbnail Available
    Item
    Analisa Material dan Job Mix Design Lapisan Surface Varian Alternatif Dengan Material Cangkang Sawit Sebagai Aggregat Kasar dan Halus
    (2013-01-12) Novan, Andre
    Cangkang sawit merupakan limbah yang sebagian besar belum termanfaatkan di daerah-daerah perkebunan di propinsi Riau. Di samping itu dae'"ah-daerah perkebunan tersebut masih memerlukan prasarana transportasi jalan yang lebih layak untuk meningkatkan kapasitas produksi. Dengan latar belakang itulah penuHs tertarik untuk melakukan penelitian yang menjadikan cangkang sawit sebagai objek, spesifiknya sebagai balian aggregat kasar/medium/halus dalam campuran panas (hot mix) lapisan perkerasan jalan. Dalam objek penelitian ada beberapa perlakuan yang diberikan kepada sampel, yang pertama melakukan Job Mix campuran panas dengan cangkang sawit sebagai aggregat kasar, medium dan halus, kedua campuran tadi diberikan variasi suhu perendaman untuk melihat sensitifitasnya terhadap suhu dan variasi penumbukan untuk mengetahui jumlah tumbukan yang ideal serta perilakunya terhadap ragam tumbukan tadi. Ketiga memberikan kombinasi cangkang sawit sebagai aggregat kasar/medium/halus dengan aggregat alam S. Kampar sebagai aggregat medium/halus. Dalam campuran kombinasi ini diberlakukan empat variasi kuantitas, variasi I 100% aggregat S. Kampar sebagai aggregat medium/halus, variasi II 75% aggregat S. Kampar sebagai aggregat medium/halus serta 25% cangkang crushed, variasi III 50% aggregat S. Kampar sebagai aggregat medium/halus serta 50% cangkang crushed dan variasi IV 25%) aggregat S. Kampar sebagai aggregat medium/halus serta 75% cangkang crushed. Dalam penelitian ini tidak dicari aspal optimum dengan kuncian spek tetapi berdasarkan angka stabilitas terbesar karena spek khusus untuk campuran type ini belum pernah ada perumusannya.
  • No Thumbnail Available
    Item
    KUAT TEKAN BETON DENGAN BAHAN TAMBAH SIKAMENT NN -DAN AGREGAT DARI DESA RANAH KECAMATAN KAMPAR
    (2014-02-06) Ermiyati; Novan, Andre
    Sikament-nn simplify the job or the workability of a liquid jet black color and can reduce the water in the concrete mix to 30%, to produce concrete of good quality while maintaining the quality of concrete sikament chemical ingredients added-NN issued by PT. SIKA with allowed dose 0.6% -1.5 % and can boost the concrete compressive strength. This research used NN sikament as an ingredient added to the concrete mixture of 0%, 1.1%, 12 %, 13%, 14% and 1.5% wight of comment with 20% water reduction, which aims to determine the optimum compressive strength with the addition of several variation of the percentage sikament NN and its influene on wordkability concrete. Test specimens used werw cylindrers with a diameter of 150 mm and height of 300m. tests done after the concrete was 28 days. The test result obtained good workability obtained at persentase 1.4% that is equal to 55 mm, whereas the heigest percentage of 1.5 % obtained in the NN Sikament of 130 mm.
  • No Thumbnail Available
    Item
    PENGARUH KUAT TEKAN BETON DENGAN PENAMBAHAN SIKAMENT NN
    (2013-05-07) Novan, Andre; Ermiyati
    Penelitian ini menggunakan penambahan dosis Sikament NN 1,5 % dari berat sement tanpa pengurangan air. Sikament NN berfungsi menambah nilai kelecekan beton dan akan mempermudah worklability Variasi pengurangan air pada penelitian ini dimulai dari 0%, 10%, 20% dan 30% terhadap kuat tekan beton, yang bertujuan untuk membuktikan pengaruh bahan tambah Sikament NN terhadap kuat tekan beton. Hasil Dari penelitian terlihat bahwa umur beton juga mempengaruhi penambahan kuat tekan beton dengan penambahan Sikament NN dengan dosis 1,5% dari berat semen pada variasi pengurangan air 20% yaitu pada umur 3 hari terjadi kenaikan kuat tekan beton sebesar 3,3% dari beton rencana, umur 14 hari terjadi kenaikan kuat tekan beton sebesar 28% dari beton rencana dan umur 28 hari terjadi kenaikan sebesar 48,13% dari beton rencana.Dengan demikian hasil pengujian ternyata Sikament NN dengan dosis 15% pada umur 28 hari dapat menebah kuat tekan beton sebesar 48,13%.