PENGARUH PERLAKUAN SUHU PADA PEMBUATAN GREEN CARBON PAPER (GCP) TANPA PEREKAT MENGGUNAKAN KULIT PISANG LILIN

Simple item page
dc.contributor.authorNoviani, Tri Mashela
dc.contributor.authorTaer, Erman
dc.contributor.authorSugianto
dc.date.accessioned2016-02-04T03:22:18Z
dc.date.available2016-02-04T03:22:18Z
dc.date.issued2016-02-04
dc.description.abstractThe making of green carbon paper (GCP) from wax banana peel by drying temperature of 140oC, 150oC and 160oC with 30 grams, 35 grams and 40 grams in mass respectively has been demonstrated. This GCP is made by using natural glue found at banana peel, namely pectin. The method of this GCP begins with weighing a sample process and grinding it for 5 minutes. The next process is molding and drying sample of 140oC, 150oC and 160oC. The measurement depicts the density of GCP with drying temperature 140oC is denser than 150oC and 160oC, whereas in 140oC the average density of 30 grams, 35 grams and 40 grams are 0,356 g/cm3, 0,432 g/cm3 and 0,630 g/cm3 respectively. For 150oC the average density of 30 grams, 35 grams and 40 grams has 0,352 g/cm3, 0,401 g/cm3, 0,460 g/cm3 respectively. For 160oC, the average density of 30 grams, 35 grams and 40 grams has 0,346 g/cm3, 0,371 g/cm3 and 0,417 g/cm3 respectively. Characterization of X-ray diffraction showed that GCP was amorphous for 140oC, 2θ = 21.052o and 45.775o, and for 160oC, 2θ = 20.429o and 46.565o. For various drying temperature, the best sample is obtained in 160oC. This is justified by the result of the energy dispersive X-ray measurement having carbon content of 83,15 %. Based on the scanning electron microscopy measurement, the best pores is shown in 160oC.en_US
dc.description.sponsorshipFakultas Matematika dan Ilmu Pengetahuan Alam Universitas Riauen_US
dc.identifier.otherwahyu sari yeni
dc.identifier.urihttp://repository.unri.ac.id/xmlui/handle/123456789/7890
dc.language.isoenen_US
dc.subjectwax banana peelen_US
dc.subjectgreen carbon paperen_US
dc.subjectpectinen_US
dc.titlePENGARUH PERLAKUAN SUHU PADA PEMBUATAN GREEN CARBON PAPER (GCP) TANPA PEREKAT MENGGUNAKAN KULIT PISANG LILINen_US
dc.typestudent Paper Post Degreeen_US

Files

Original bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
tri marshela.pdf
Size:
849.56 KB
Format:
Adobe Portable Document Format
Description:
artikel
Download
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
license.txt
Size:
1.71 KB
Format:
Item-specific license agreed upon to submission
Description:
Download

Collections

Physics